XLPE (CROSS LINKED POLYETHYLENE)

PEXCHEM®

XLPE (Cross Linked Polyethylene) for Low Voltage Energy Cables raw materials production was implemented by Özşahin, for the first time in Turkey with 100 % domestic capital. Serial production facilities started up in Dudullu manufacturing plant in 2012.

Our raw material production named as Pexchem®, has been tested and approved by all standards of TSE Laboratories and has gained great appreciation by all local consumers.

Pexchem® has also been tested by XLPE raw material quality tests, both HotSet and Schrinkage and proved higher quality values than its top competitors.

As Özşahin, we are capable in taking custom orders and requests for production. Thanks to our years of experience, technical knowledge, laboratory and machineries we are able to work in accordance, covering all demands of any tailor- made orders.

  FINISHED CABLE UNIT STANDARD VALUE
  Tensile Strength N/mm2 IEC 811 >15
  Elongation at Break % IEC 811 >500
  Elongation at Break % IEC 811 <2
  Volume Resistivity Ohm.cm ASTM D257 >1016
  Dielectric Constant Under 25°C 50%RH - ASTM D150 2,31
  Heat Ageing Properties (7 Day at 135°) min. N/mm2 TS HD 603 22,60
  Maximum Variation of Tensile Strength After Ageing (Without Conductor)
(7 days at 135°C)
% TS HD 603 8
  Maximum Variation of Elongation After Ageing (Without Conductor)
(7 days at 135°C)
% TS HD 603 -10
  Maximum Variation of Tensile Strength After Ageing (Without Conductor)
(7 days at 135°C)
% TS HD 603 -18
  Maximum Variation of Elongation After Ageing (Without Conductor)
(7 days at 135°C)
% TS HD 603 9
  Hot Set Test 20N/cm2 (With Load) (15 min 200 ˚C) % TS HD 603 175
  Hot Set Test 20N/cm2 (Without Load) (15 min 200 ˚C) % TS HD 603 15
  Bending Test (10 days at 150°C) - IEC 811 Comply
  MATERIALS OF CABLE INDUSTRY
   
PEXCHEM® XLPE
   
  COMPOUND UNITY STANDARD VALUE
  Density g/cm3 ASTM D792 0,92
  Melt Index g/10 min ASTM D1238 1,6
  Moisture ppm OWN <200
  Shelf LifeT months OWN 12

Click to download the XLPE Brochure